Rheological measurements for characterization of polyolefins: low-density polyethylene (LDPE) for extrusion coating ,Test Method TAPPI/ANSI T 702 om-14

Please Note: This document will be available in PDF format in the "My Electronic Documents" link on the home page once your order has been completed. Please make sure you have the latest version of Acrobat Reader. Click on the Acrobat Reader icon to check for the latest version, it’s FREE. To print a hardcopy of a PDF file correctly you must have a postscript printer. If you are not sure if your printer is a postscript printer please refer to your owner’s manual.

In extrusion coating a thin molten polymer film is coated on some kind of substrate. At high extrusion coating speed, even a minor disturbance on the melt web causes major quality problems, which very rapidly lead to large quantities of waste. Therefore, higher coating speeds require polymers with high and even quality in order to avoid waste due to polymer edge instability and web break.

The rheology-related phenomena that may cause problems in extrusion coating are neck-in (NI) and draw-down (DD). The neck-in is the reduction of the film width and may cause uncoated areas on the substrate. The neck-in is less if the melt elasticity is high. The draw-down is the ability of the melt to be drawn to thin films without breaking. Draw-down is favored by a melt that is more viscous than elastic.

Changes in the molecular structure have a great impact on the rheological and processing properties of a polymer. Storage modulus and zero shear viscosity have been found to be useful parameters to predict the extrusion coating performance of LDPE. Storage modulus quantifies a material’s ability to store energy elastically and so to deform under stress. As the storage modulus increases, the ability of the material to deform decreases. Zero shear viscosity is related to molecular weight; a small change in molecular weight results in a big change of zero shear viscosity. Knowing this, there is a relation between storage modulus, zero shear viscosity, draw down and neck-in. As storage modulus and zero shear viscosity increase, neck-in decreases and so does the draw down capacity, meaning a lower line speed at which the polymer can be drawn down to a desired thickness.

Rheological measurements for characterization of polyolefins
Rheological measurements for characterization of polyolefins: low-density polyethylene (LDPE) for extrusion coating ,Test Method TAPPI/ANSI T 702 om-14

New Releases


Kraft Recovery Boilers, Third Edition  

Sponsored by the Recovery Boiler Program R&D Subcommittee of the American Forest & Paper Association (AF&PA) and published by TAPPI Press.



Handbook For Pulp and Paper Technologists (The SMOOK Book), Fourth Edition

The best-selling text to introduce the entire technology of pulp and paper manufacture.



Guidelines for Safe Assessment and Operation of Yankee Dryers  

A project of the Yankee Dryer Safety & Reliability Committee.



Check our newest additions.

TAPPI Press offers some of the most in-depth resources and references for the forest products and related industries. 

See More


Available for Purchase – Conference Proceedings

TAPPI maintains a record of key conference papers, presentations, and other conference publications, available for purchase in a variety of formats.

See More