Critical Pigment Volume Concentration Concept for Paper Coatings: I. Model Coating Systems Using Plastic Pigments and Latex Binders for Paper Coating..., 1998 Coating Conference Proceedings

Please Note: This document will be available in PDF format in the "My Electronic Documents" link on the home page once your order has been completed. Please make sure you have the latest version of Acrobat Reader. Click on the Acrobat Reader icon to check for the latest version, it’s FREE. To print a hardcopy of a PDF file correctly you must have a postscript printer. If you are not sure if your printer is a postscript printer please refer to your owner’s manual.

The immobilization and consolidation of the model coatings based on the plastic pigment and latex binder of known particle sizes were theoretically studied in terms of the dense random packing of binary spheres and varying extent of latex film shrinkage. The porosity of the model coatings was calculated based on three proposed latex shrinkage models: Maximum, Minimum, and Linearly Decreasing Latex Shrinkage. The increasing extent of latex shrinkage was calculated up to the critical pigment volume concentration (CPVC) as a function of plastic pigment volume fractions, and the maximum latex shrinkage was estimated from the CPVC. Also, the number of pores and the average equivalent spherical pore diameters were calculated based on those proposed models. The opacity and gloss of the model coatings on polyester films were measured and their porosity was also determined by a simple coat weight-thickness method. As expected, various coating structure-property-composition relationships, such as opacity, gloss, porosity, etc., were shown to exhibit sharp transitions near the CPVC. The CPVC values determined by the opacity, gloss, and porosity vs. PVC relationships, respectively, agreed very well with each other. Especially, the CPVC’s determined by the opacity and porosity vs. PVC curves were identical. The comparison between the theoretically calculated and experimental porosity values showed that the intermediate value between the maximum and minimum latex shrinkage would best fit the experimental porosity data. The effect of plastic pigment particle size on the optical properties and porosity of model coatings was also studied and it was observed that the coating opacity and porosity increased with increasing plastic pigment particle size, but the gloss decreased. The ink gloss of the uncalendered model coatings applied onto commercial sheet offset coated papers was shown to be affected by both the coating gloss and porosity: the higher the coating gloss, the higher the ink gloss, but the higher the coating porosity, the lower the ink gloss. Their printability was also studied in terms of the number of passes-to-fail and the rate of ink setting as a function of both plastic pigment volume fractions and plastic pigment particle sizes. A minimum crack-free temperature (MCFT) of latex-bound coatings was proposed to better predict the behaviors of latexes as coating binders. The wet state of model coating dispersions, the surfaces of consolidated model coatings, and their internal structure were examined by both electron and atomic force microscopy, and their micrographs were found to be consistent with our immobilization and consolidation models.